Pipes

Pipes
You can easily find the products you need by subcategories and using the navigation filter. Any product you want to download in PDF can be added by selecting it in the catalog.
Polyethylene
Segment
Pipes
Processing Method
Extrusion
Areas of use
Pressure pipes and fittings for domestic water supply and gas distribution networks
MFI (g/10 min)
0,25 (5 kg)
Density (g/cm3)
0.959
Type of polymer
High-density polyethylene (HDPE)
Special additives
Enhanced stabilization, UV stabilizer
Principal characteristics
A bimodal product of PE100 class. Long service life, high hydrolytic strength. UV resistant.
Min flexural modulus (MPa)
1000
Segment
Pipes
Processing Method
Extrusion
Areas of use
Pressure pipes and fittings for an alternative method of laying according to PAS 1075 in domestic water supply and gas distribution networks
MFI (g/10 min)
0.30 (5 kg)
Density (g/cm3)
0.959
Type of polymer
High-density polyethylene (HDPE)
Special additives
Enhanced stabilization, UV stabilizer
Principal characteristics
A bimodal product of PE100 class. Long service life, high hydrolytic strength. UV resistant. High resistance to crack propagation.
Min flexural modulus (MPa)
1000
Segment
Pipes
Processing Method
Extrusion
Areas of use
Pressure intra-house pipes for water supply and underfloor heating
MFI (g/10 min)
12.5 (at 21.6 kg)
Density (g/cm3)
0.938
Type of polymer
High-density polyethylene (HDPE)
Special additives
Enhanced stabilization
Principal characteristics
PE-RT Type 1 PE80 class product
Segment
Pipes
Processing Method
Extrusion
Areas of use
General-purpose pipes
MFI (g/10 min)
8.5 (at 21.6 kg)
Density (g/cm3)
0.949
Type of polymer
High-density polyethylene (HDPE)
Special additives
Enhanced stabilization
Principal characteristics
A bimodal product similar to PE100. Long service life, high hydrolytic strength.
Polypropylene
Segment
Pipes;
Animal house
Processing Method
Extrusion
Areas of use
Inhouse non-pressure pipes and fittings
MFI (g/10 min)
0.70
Min flexural modulus (MPa)
1300
Type of polymer
Polypropylene Homopolymer (PPH)
Special additives
Enhanced stabilization
Principal characteristics
Increased melt strength
Segment
Pipes
Processing Method
Extrusion
Areas of use
Inhouse non-pressure pipes and fittings
MFI (g/10 min)
3.0
Min flexural modulus (MPa)
1400
Type of polymer
Polypropylene Homopolymer (PPH)
Special additives
Basic recipe
Principal characteristics
Basic stabilization recipe
Segment
Pipes
Processing Method
Extrusion
Areas of use
Corrugated pipes
MFI (g/10 min)
0.30 (2.16 kg)
Min flexural modulus (MPa)
1450
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Enhanced stabilization
Principal characteristics
High impact strength. Available for installation at temperatures below zero
Segment
Pipes
Processing Method
Extrusion
Areas of use
Domestic pressure pipes and fittings for water supply and heating
MFI (g/10 min)
0.30 (2.16 kg)
Min flexural modulus (MPa)
800
Type of polymer
Polypropylene Random Copolymer (PPR)
Special additives
Enhanced stabilization
Principal characteristics
Hydrolytic strength
Optimal solutions for partners