Plastics modification
Plastics modification
You can easily find the products you need by subcategories and using the navigation filter. Any product you want to download in PDF can be added by selecting it in the catalog.
Lithium butadiene rubber
Segment
Plastics modification
Areas of use
Intended for use in the synthesis of high-impact polystyrene.
Mass fraction of ash (%), NMT
0.1
Mooney viscosity UML (1+4), 100 °C (Mooney units)
35-55
Mooney viscosity spread within the batch (Mooney units), NMT
6
Loss on drying (%), NMT
0.6
Mass fraction of dry gel (5.43% by weight solution of rubber in toluene) (%), NMT
0.02
Viscosity (5.43 % by weight of the rubber solution in toluene)(MPa s), range
30-100
Pt/Co сolority (5.43 % by weight of the rubber solution in toluene) (Hazen), NMT
10
Mass fraction of 1,2-links (%), range
10.0–15.0
Mass fraction of 1,4-cis links (%), range
34.0–40.0
Mass fraction of antioxidant of non-coloring type (%), NLT
0.1
Segment
Plastics modification
Areas of use
Intended for use in the synthesis of high-impact polystyrene.
Mass fraction of ash (%), NMT
0.1
Mooney viscosity spread within the batch (Mooney units), NMT
6
Loss on drying (%), NMT
0.6
Mass fraction of dry gel (5.43% by weight solution of rubber in toluene) (%), NMT
0.02
Viscosity (5.43 % by weight of the rubber solution in toluene)(MPa s), range
151-200
Pt/Co сolority (5.43 % by weight of the rubber solution in toluene) (Hazen), NMT
10
Mass fraction of 1,2-links (%), range
10.0–15.0
Mass fraction of 1,4-cis links (%), range
34.0–40.0
Mass fraction of antioxidant of non-coloring type (%), NLT
0.1
Mooney viscosity, MB 1+4 (100 °C) (Mooney units), range
45-65
Segment
Plastics modification
Areas of use
Intended for use in the synthesis of high-impact polystyrene.
Mass fraction of ash (%), NMT
0.1
Mooney viscosity spread within the batch (Mooney units), NMT
6
Loss on drying (%), NMT
0.6
Mass fraction of dry gel (5.43% by weight solution of rubber in toluene) (%), NMT
0.02
Viscosity (5.43 % by weight of the rubber solution in toluene)(MPa s), range
201-280
Pt/Co сolority (5.43 % by weight of the rubber solution in toluene) (Hazen), NMT
10
Mass fraction of 1,2-links (%), range
10.0–15.0
Mass fraction of 1,4-cis links (%), range
34.0–40.0
Mass fraction of antioxidant of non-coloring type (%), NLT
0.1
Mooney viscosity, MB 1+4 (100 °C) (Mooney units), range
65-75