Household appliances, electronics, toys, tool making
Household appliances, electronics, toys, tool making
You can easily find the products you need by subcategories and using the navigation filter. Any product you want to download in PDF can be added by selecting it in the catalog.
SBS
Segment
Household appliances, electronics, toys, tool making;
Footwear;
Cable insulation
Footwear;
Cable insulation
Areas of use
Footwear, cable, household articles
Benefits, in relation to segments/processing methods
High absorption rate and oil distribution quality
Mass fraction of volatile substances (%), NMT
≤ 0.8
Bound styrene content (%)
30±1.5
Breaking elongation (%), NLT
≥ 550
Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt
26 ±4
Melt flow index, 190 °C/5 kgf (g/10 min)
<1
Nominal tensile strength (MPa)
≥ 8.0
Elasticity modulus 300% (MPa)
≥ 2.0
Shore A hardness (c.u.)
82 ±5
Principal characteristics
Increased thermal stability, high porosity, improved mechanical properties, the greatest effect is achieved when combined with a radial K grade
Additional parameters
OIT — 180 °C
ABS plastic
Segment
Household appliances, electronics, toys, tool making;
Automotive components
Automotive components
Processing Method
Extrusion
Areas of use
For the production of sheets with high surface quality (co-extruded or not and with high extrusion multiplicity) for various applications such as refrigeration, plumbing, automotive, packaging and furniture industry (profiles)
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
4.0 ±1.5
Min Vicat softening temperature (°C)
100
Tear resistance (MPa), NLT
45
Izod impact strength, notched (J/m), NLT
15
Bending strength (MPa), NLT
68
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
60
Principal characteristics
Good rigidity and strength balance
Segment
Household appliances, electronics, toys, tool making;
Automotive components
Automotive components
Processing Method
Extrusion
Areas of use
Used for thick-sheet extrusion (co-extruded or not) for plumbing and transport products. The grade is produced only in natural color, with no additives or colors
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
4.5 ±1.5
Min Vicat softening temperature (°C)
100
Izod impact strength, notched (J/m), NLT
20
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
60
Principal characteristics
Very high-impact grade for sheet extrusion with high processability and improved heat resistance
Segment
Household appliances, electronics, toys, tool making;
Automotive components
Automotive components
Processing Method
Extrusion
Areas of use
For the production of large sheet with high surface quality (co-extruded or not and with high extrusion multiplicity) for various applications, such as the refrigeration industry, plumbing, automotive, packaging and furniture industry (profiles)
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
5.0 ±1.5
Min Vicat softening temperature (°C)
100
Tear resistance (MPa), NLT
35
Izod impact strength, notched (J/m), NLT
16.5
Bending strength (MPa), NLT
68
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
60
Principal characteristics
High strength and rigidity, as well as high heat resistance
Segment
Household appliances, electronics, toys, tool making;
Manufacture of sanitary ware and panels;
Automotive components
Manufacture of sanitary ware and panels;
Automotive components
Processing Method
Thermal molding
Areas of use
Used in the automotive industry for interior decoration components.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
10.0 ±1.5
Min Vicat softening temperature (°C)
98
Tear resistance (MPa), NLT
40
Izod impact strength, notched (J/m), NLT
10
Bending strength (MPa), NLT
62
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
50
Principal characteristics
Average heat resistance, high fluidity and impact resistance, improved heat resistance during processing
Segment
Household appliances, electronics, toys, tool making
Processing Method
Extrusion
Areas of use
Used in the automotive industry for interior decoration components.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
10.0 ±1.5
Min Vicat softening temperature (°C)
98
Tear resistance (MPa), NLT
40
Izod impact strength, notched (J/m), NLT
10
Bending strength (MPa), NLT
62
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
50
Principal characteristics
Average heat resistance, high fluidity and impact resistance, improved heat resistance during processing
Segment
Household appliances, electronics, toys, tool making;
Manufacture of sanitary ware and panels;
Automotive components
Manufacture of sanitary ware and panels;
Automotive components
Processing Method
Thermal molding
Areas of use
Used in the production of small and large household appliances, vacuum cleaners, toys, phones and consumer electronics.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
23 ±3.0
Min Vicat softening temperature (°C)
90
Izod impact strength, notched (J/m), NLT
11
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
60
Principal characteristics
Injection molding general-purpose grade with high fluidity, combines high impact strength with excellent gloss