Heat and sound insulation
Heat and sound insulation
You can easily find the products you need by subcategories and using the navigation filter. Any product you want to download in PDF can be added by selecting it in the catalog.
Foaming suspension polystyrene
Segment
Heat and sound insulation;
Barrier structures
Barrier structures
Processing Method
Foaming
Areas of use
Low- and medium-density self-extinguishing heat and sound insulation boards. Polystyrene concrete.
Pellet size (mm)
1.4–2.2
Basic fraction share (%)
99
Mass fraction of pentane (%)
5–7
Moisture content, NMT (%)
1
Mass fraction of monomer (%)
0.1
Segment
Heat and sound insulation;
Heat insulation layers, light earth fills
Heat insulation layers, light earth fills
Processing Method
Foaming
Areas of use
Styrofoam blocks for light earth fills during road construction. Low- and medium-density self extinguishing heat and sound insulation boards. Polystyrene concrete.
Pellet size (mm)
0.96–1.6
Basic fraction share (%)
99
Mass fraction of pentane (%)
5–7
Moisture content, NMT (%)
1
Mass fraction of monomer (%)
0.1
Segment
Heat and sound insulation;
Heat insulation layers, light earth fills;
Packaging elements for household appliances
Heat insulation layers, light earth fills;
Packaging elements for household appliances
Processing Method
Foaming
Areas of use
Medium-density self-extinguishing thermal insulation boards. Molding products with a thickness of over 10 mm. Ceiling slabs and baseboards. Styrofoam blocks for light earth fills during road construction. Polystyrene concrete.
Pellet size (mm)
0.7–1.0
Basic fraction share (%)
98
Mass fraction of pentane (%)
5–7
Moisture content, NMT (%)
1
Mass fraction of monomer (%)
0.1
Segment
Heat and sound insulation;
Packaging elements for household appliances
Packaging elements for household appliances
Processing Method
Foaming
Areas of use
Medium- and high-density self-extinguishing heat and sound insulation boards. Molding products. Ceiling slabs and baseboards. Decorative products.
Pellet size (mm)
0.45–0.7
Basic fraction share (%)
99
Mass fraction of pentane (%)
5–7
Moisture content, NMT (%)
1
Mass fraction of monomer (%)
0.1
Segment
Heat and sound insulation;
Packaging elements for household appliances
Packaging elements for household appliances
Processing Method
Foaming
Areas of use
Medium- and high-density self-extinguishing heat and sound insulation boards. Molding products. Ceiling slabs and baseboards. Decorative products
Pellet size (mm)
0.3–0.45
Basic fraction share (%)
99
Mass fraction of pentane (%)
5–7
Moisture content, NMT (%)
1
Mass fraction of monomer (%)
0.1
Polystyrene
Segment
Heat and sound insulation
Processing Method
Extrusion
Areas of use
For the manufacture of foamed products by extrusion.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
1.6 ±0.4
Min Vicat softening temperature (°C)
97
Principal characteristics
High-strength grade of GPPS without mineral oil additive with improved strength properties
Tear resistance (MPa), NLT
47
Bending strength (MPa), NLT
92
Mass fraction of residual styrene (%), NMT
0.05
Segment
Heat and sound insulation
Processing Method
Extrusion
Areas of use
For the manufacture of foamed products by extrusion.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
7.0 ±2.0
Min Vicat softening temperature (°C)
100
Tear resistance (MPa), NLT
45
Bending strength (MPa), NLT
88
Mass fraction of residual styrene (%), NMT
0.05
Segment
Heat and sound insulation
Processing Method
Extrusion
Areas of use
For the manufacture of foamed products by extrusion.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
21.0 ±4.0
Min Vicat softening temperature (°C)
90
Tear resistance (MPa), NLT
37
Bending strength (MPa), NLT
58
Mass fraction of residual styrene (%), NMT
0.05
Segment
Heat and sound insulation
Processing Method
Extrusion
Areas of use
For the manufacture of foamed extruded polystyrene sheet or decorative foamed interior products.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
30.0 ±5.0
Min Vicat softening temperature (°C)
88
Principal characteristics
High-flow grade of GPPS without mineral oil
Tear resistance (MPa), NLT
35
Bending strength (MPa), NLT
55
Mass fraction of residual styrene (%), NMT
0.05
Segment
Heat and sound insulation
Processing Method
Extrusion
Areas of use
For the manufacture of foamed products by extrusion and for the production of XPS with enhanced resistance to damage.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
7.0 ±2.0
Min Vicat softening temperature (°C)
96
Principal characteristics
Medium-flowing PS
Tear resistance (MPa), NLT
37
Bending strength (MPa), NLT
80
Mass fraction of residual styrene (%), NMT
0.05
Segment
Heat and sound insulation
Processing Method
Extrusion
Areas of use
For the manufacture of foamed products by extrusion.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
2.5 ±2.0
Min Vicat softening temperature (°C)
100
Tear resistance (MPa), NLT
38
Bending strength (MPa), NLT
90
Mass fraction of residual styrene (%), NMT
0.05
Segment
Heat and sound insulation
Processing Method
Extrusion
Areas of use
For the manufacture of foamed products by extrusion and for the production of polystyrene sheets.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
2.5 ±1.0
Min Vicat softening temperature (°C)
95
Principal characteristics
Low-flow heat resistant PS with high molecular weight
Tear resistance (MPa), NLT
25
Bending strength (MPa), NLT
70
Mass fraction of residual styrene (%), NMT
0.05
Segment
Heat and sound insulation
Processing Method
Extrusion
Areas of use
For the manufacture of foamed products by extrusion.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
1.8 ±0.2
Min Vicat softening temperature (°C)
102
Principal characteristics
High-strength grade of low-flow GPPS with high molecular weight and improved strength properties
Tear resistance (MPa), NLT
50
Bending strength (MPa), NLT
95
Mass fraction of residual styrene (%), NMT
0.05