Automotive components
Automotive components
You can easily find the products you need by subcategories and using the navigation filter. Any product you want to download in PDF can be added by selecting it in the catalog.
Polypropylene
Segment
Automotive components
Processing Method
Injection molding
Areas of use
Compounding, automotive products
MFI (g/10 min)
30
Min flexural modulus (MPa)
1150
Min Izod impact strength, J/m
at 23 ̊C, 77 at -20 ̊C — not standardized
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Nucleating agent, antistatic additive
Principal characteristics
Improved stress-strain properties, for the production of polymer products with high resistance to cracking and frost resistance (increased flexural modulus)
Segment
Automotive components
Processing Method
Injection molding
Areas of use
Compounds for exterior, interior and engine compartment parts
MFI (g/10 min)
3.0 (2.16 kg)
Min flexural modulus (MPa)
1300
Type of polymer
Polypropylene Homopolymer (PPH)
Special additives
Basic stabilization recipe
Principal characteristics
Basic grade
Segment
Automotive components
Processing Method
Compounding
Areas of use
Compounds for exterior, interior and engine compartment parts
MFI (g/10 min)
25
Min flexural modulus (MPa)
1500
Type of polymer
Polypropylene Homopolymer (PPH)
Special additives
Basic stabilization recipe
Principal characteristics
Basic grade
Segment
Automotive components
Processing Method
Compounding
Areas of use
Compounds for the manufacture of exterior, interior and engine compartment parts
MFI (g/10 min)
35
Min flexural modulus (MPa)
1500
Type of polymer
Polypropylene Homopolymer (PPH)
Special additives
Basic stabilization recipe
Principal characteristics
Basic grade
Segment
Automotive components
Processing Method
Injection molding
Areas of use
Compounds for the manufacture of exterior, interior and engine compartment parts
MFI (g/10 min)
45
Min flexural modulus (MPa)
1500
Type of polymer
Polypropylene Homopolymer (PPH)
Special additives
Basic stabilization recipe
Principal characteristics
Basic grade
Segment
Automotive components;
Containers for seedlings
Containers for seedlings
Processing Method
Injection molding
Areas of use
Vehicle components
MFI (g/10 min)
12
Min flexural modulus (MPa)
1000
Min Izod impact strength, J/m
23 ̊C – 85; -20 ̊C – 35; -40 ̊C – not determined
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Basic recipe
Principal characteristics
Increased long-term thermal stability, resistance to thermo-oxidative degradation during processing and final product use
Segment
Automotive components
Processing Method
Extrusion blow molding
Areas of use
Battery housings, automotive products made by extrusion and blow molding
MFI (g/10 min)
1.6
Min flexural modulus (MPa)
1350
Min Izod impact strength, J/m
at 23 ̊C 500 at -20 ̊C — not standardized at -40 ̊C – not determined
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Nucleating agent, antistatic additive
Principal characteristics
Improved stress-strain properties, for the production of polymer products with high resistance to cracking and frost resistance
Segment
Automotive components
Processing Method
Injection molding
Areas of use
Battery cases, finishing materials for luggage bags, cables and wires
MFI (g/10 min)
8
Min flexural modulus (MPa)
1100
Min Izod impact strength, J/m
23 ̊C – 90; -20 ̊C – 35; -40 ̊C – not determined
Type of polymer
Polypropylene Block Copolymer (PPB)
Principal characteristics
Increased long-term thermal stability, improved resistance to thermal oxidative degradation in PP processing and product use
Segment
Automotive components
Processing Method
Compounding
Areas of use
Compounds for exterior, interior and engine compartment parts
MFI (g/10 min)
12
Min flexural modulus (MPa)
1350
Min Izod impact strength, J/m
-
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Nucleating agent
Principal characteristics
A special grade with balanced rigidity and impact resistance
Segment
Automotive components
Processing Method
Injection molding
Areas of use
Automotive products
MFI (g/10 min)
12.5
Min flexural modulus (MPa)
1300
Min Izod impact strength, J/m
at 23 ̊C, 85 at -20 ̊C — not standardized at -40 ̊C – not determined
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
-
Principal characteristics
Improved stress-strain properties for the production of polymer products with high resistance to cracking and frost resistance (increased flexural modulus)
Segment
Automotive components
Processing Method
Compounding
Areas of use
Compounds for exterior, interior and engine compartment parts
MFI (g/10 min)
45
Min flexural modulus (MPa)
1500
Min Izod impact strength, J/m
-
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Nucleating agent, antistatic additive
Principal characteristics
A special grade for high-speed casting with high processing speed, increased rigidity, low warping
Segment
Automotive components
Processing Method
Injection molding
Areas of use
Automotive parts
MFI (g/10 min)
42
Min flexural modulus (MPa)
1200
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Nucleating agent, antistatic additive
Principal characteristics
A special grade for high-speed casting with high processing speed, increased rigidity, low warping
Segment
Rigid packaging;
Automotive components;
Food-grade containers, Water containers
Automotive components;
Food-grade containers, Water containers
Processing Method
Injection molding
Areas of use
Packaging, buckets, containers, kitchenware
MFI (g/10 min)
80
Min flexural modulus (MPa)
1300
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Nucleating agent, antistatic additive
Principal characteristics
Improved stress-strain properties (flexural modulus and impact resistance balance)
Segment
Automotive components
Processing Method
Injection molding
Areas of use
Vehicle components
MFI (g/10 min)
11.5
Min flexural modulus (MPa)
1000
Min Izod impact strength, J/m
at 23 ̊C, 400 at -20 ̊C, 60 at -40 ̊C – not determined
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Nucleating agent
Principal characteristics
Increased resistance to thermal oxidative degradation in the PP production process
Segment
Automotive components
Processing Method
Injection molding
Areas of use
Vehicle components
MFI (g/10 min)
20
Min flexural modulus (MPa)
850
Min Izod impact strength, J/m
at 23 ̊C, 500 at — 20 ̊C, 80
Type of polymer
Polypropylene Block Copolymer (PPB)
Special additives
Nucleating agent, impact strength modifier
Principal characteristics
A special grade for casting with high impact resistance
ABS plastic
Segment
Household appliances, electronics, toys, tool making;
Automotive components
Automotive components
Processing Method
Extrusion
Areas of use
For the production of sheets with high surface quality (co-extruded or not and with high extrusion multiplicity) for various applications such as refrigeration, plumbing, automotive, packaging and furniture industry (profiles)
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
4.0 ±1.5
Min Vicat softening temperature (°C)
100
Tear resistance (MPa), NLT
45
Izod impact strength, notched (J/m), NLT
15
Bending strength (MPa), NLT
68
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
60
Principal characteristics
Good rigidity and strength balance
Segment
Household appliances, electronics, toys, tool making;
Automotive components
Automotive components
Processing Method
Extrusion
Areas of use
Used for thick-sheet extrusion (co-extruded or not) for plumbing and transport products. The grade is produced only in natural color, with no additives or colors
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
4.5 ±1.5
Min Vicat softening temperature (°C)
100
Izod impact strength, notched (J/m), NLT
20
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
60
Principal characteristics
Very high-impact grade for sheet extrusion with high processability and improved heat resistance
Segment
Household appliances, electronics, toys, tool making;
Automotive components
Automotive components
Processing Method
Extrusion
Areas of use
For the production of large sheet with high surface quality (co-extruded or not and with high extrusion multiplicity) for various applications, such as the refrigeration industry, plumbing, automotive, packaging and furniture industry (profiles)
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
5.0 ±1.5
Min Vicat softening temperature (°C)
100
Tear resistance (MPa), NLT
35
Izod impact strength, notched (J/m), NLT
16.5
Bending strength (MPa), NLT
68
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
60
Principal characteristics
High strength and rigidity, as well as high heat resistance
Segment
Household appliances, electronics, toys, tool making;
Manufacture of sanitary ware and panels;
Automotive components
Manufacture of sanitary ware and panels;
Automotive components
Processing Method
Thermal molding
Areas of use
Used in the automotive industry for interior decoration components.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
10.0 ±1.5
Min Vicat softening temperature (°C)
98
Tear resistance (MPa), NLT
40
Izod impact strength, notched (J/m), NLT
10
Bending strength (MPa), NLT
62
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
50
Principal characteristics
Average heat resistance, high fluidity and impact resistance, improved heat resistance during processing
Segment
Household appliances, electronics, toys, tool making;
Manufacture of sanitary ware and panels;
Automotive components
Manufacture of sanitary ware and panels;
Automotive components
Processing Method
Thermal molding
Areas of use
Used in the production of small and large household appliances, vacuum cleaners, toys, phones and consumer electronics.
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
23 ±3.0
Min Vicat softening temperature (°C)
90
Izod impact strength, notched (J/m), NLT
11
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
60
Principal characteristics
Injection molding general-purpose grade with high fluidity, combines high impact strength with excellent gloss
Segment
Automotive components
Processing Method
Thermal molding
Areas of use
Used in the automotive industry for the production of interior components (extruded profile, interior trim details, etc.) and with the appropriate coating to obtain exterior trim components (grilles, mirrors, etc.)
Melt flow rate range, g/10min. (at 220 °C, 5kg load)
6.0 ±1.5
Min Vicat softening temperature (°C)
104
Tear resistance (MPa), NLT
43
Izod impact strength, notched (J/m), NLT
12
Bending strength (MPa), NLT
65
Mass fraction of residual styrene (%), NMT
0.05
Gloss at 60˚ angle, NLT
60
Principal characteristics
High fluidity and impact resistance, as well as improved heat resistance during processing